Note: Please keep the powder in vacuum box to avoid moisture.
Please bake the powder in vacuum oven at 120 0C – 150 0C before making slurry and coating to ensure maximum capacity.
SPECIFICATION:
| Granularity | D10: ≥ 8 μm D50: 16.5 – 19 μm D90: ≤ 32 μm |
| Surface Area | ≤ 1.5 m2/g |
| Tap Density | ≥ 1.28 g/cm3 |
| Moisture | ≤ 0.05 % |
| First Discharge Capacity | ≥ 320 mAh/g |
| First Discharge Rate | ≥ 91 % |
| Fe | ≤ 50 ppm |
SPECIFICATION:
| Chemical Formula | Li4Ti5O12 |
| Granularity | D10 : 0.2 µmD50 : 1.0 µmD90 : ≤ 3.0 µm |
| pH Value | ≤ 11.5 |
| Pressed Density | ≥ 1.20 g/cm3 |
| Specific Surface Area | 1.0 – 2.0 m2/g |
| First discharge Capacity | 165 – 70 mAh/g (0.8 – 2.7 V, 0.2C Button half open cell) |
| First Discharge efficiency | ≥ 99.7 % |
| Appearance | White Powder, No Agglomeration, No Sundries |
| Storage Safety | Avoid moist |
DESCRIPTION:
Natural graphite powder is black powder, with good cycle performance, particle shape is spherical, uniform particle size distribution, and with high graphitization degree.
Note: Please keep the powder in vacuum box to avoid moisture.
Please bake the powder in vacuum oven at 120 0C – 150 0C before making slurry and coating to ensure maximum capacity.
Specifications:
| Granularity | D10 : 10 – 13 μm D50 : 18 – 20 μm D90 : 28 – 32 μm |
| Tap Density | 1.10 ~ 1.20 g/cm3 |
| Pressed Density | 1.60 – 1.65 g/cm3 |
| Specific Surface Area | 2.5 ~ 3.5 m2/g |
| Fe | ≤ 5 ppm |
| Cr | ≤ 2 ppm |
| Zn | ≤ 2 ppm |
| Ni | ≤ 2 ppm |
| Moisture | < 0.1% |
| Ash | < 0.02% |
| First Discharge Capacity | 360 ~ 370 mAh/g |
| Cycle Life | Cycle 500, the capacity >88% |
| Appearance | Black Powder, No Agglomeration, No Sundries |
Description: Artificial graphite is a black powder and suitable for making anode of Li ion battery.
Note:Please keep the powder in vacuum box to avoid moisture and bake the powder in a vacuum oven at 120 – 150 °C before making slurry and coating to ensure max. capacity.
Specifications:
| Granularity | D10 : 10 – 13 μm D50 : 18 – 20 μm D90 : 28 – 32 μm |
| Tap Density | 1.10 ~ 1.20 g/cm3 |
| Pressed Density | 1.60 – 1.65 g/cm3 |
| Specific Surface Area | 2.5 ~ 3.5 m2/g |
.
Description: High Surface area active carbon is extra high surface area active carbon powder for preparing electrode of high power super capacitor.
Specifications
| BET surface area(m2/g) | 2000(±100) |
| Bulk density (g/cc) | 0.32-0.40 |
| Pore Volume (cm^3/g) | 0.9±0.1 |
| Pore Size | 2.0-2.2mm |
| Iodine Absorption (mg/g) | 2000(±100) |
| Particle size D50 (μm) | 5 (±1) |
| PH | 6.0-7.0 |
| Carbon(%) | >95 |
| Ash(%) | <0.07 |
| Ions from ICP(ppm) | <1000 |
| Organic capacitance (F/g) (Note1) | >132 |
| Organic capacitance (F/cc) (Note2) | >62 |
| Inorganic capacitance (F/g) (Note3) | >240 |
| Inorganic capacitance (F/cc) (Note2) | >120 |