LiNiMnCoO2 (Lithium Nickel Manganese Cobalt Oxide) powder is used for Ultra-high capacity Li-ion battery cathode material.
Note: Please keep the powder in vacuum box to avoid moisture.
Please bake the powder in vacuum oven at 120 0C – 150 0C before making slurry and coating to ensure maximum capacity.
SPECIFICATIONS:
| Chemical Formula | LiNiMnCoO2 |
| Ni:Co:Mn | 5:2:3 |
| Ni + Co + Mn | ≥57.17 % |
| Li | 7.00 – 8.00 % |
| H2O | ≤0.1% |
| Granularity | D10 : ≥ 5.0 µm D50 : 8.0 – 12.0 µm D90 : ≤ 25.0 µm |
| pH Value | ≤ 11.00 |
| Pressed Density | ≥ 2.30 g/cm2 |
| Specific Surface Area | 0.20 – 0.50 m2/g |
| First Discharge Capacity | ≥ 155 mAh/g (0.2C, 4.2 – 3.0V, button half open cell |
| First Discharge efficiency | 89 – 90% |
| Appearance | Black Powder, No Agglomeration, No Sundries |
| Storage Safety | Avoid moist |
LiMn2O4 (Lithium Manganese Oxide) powder is used for Li-ion battery cathode material.
Note: Please keep the powder in vacuum box to avoid moisture.
Please bake the powder in vacuum oven at 120 0C – 150 0C before making slurry and coating to ensure maximum capacity.
SPECIFICATIONS:
| Chemical Formula | LiMn2O4 |
| Granularity | D10 : > 4.0 µmD50 : 13.0 ~ 17 µmD90 : <350 µm |
| Pressed Density | > 2.0 g/cm3 |
| Specific Surface Area | 0.4 ~ 1.0 m2/g |
| Mn | 56.5 ~ 58.9 % |
| Fe | < 0.02 % |
| Cu | < 0.02 % |
| Zn | < 0.02 % |
| Ca | < 0.03 % |
| Ni | < 0.03 % |
| pH Value | < 11 |
| Moisture | < 1000 ppm |
| Capacity | > 102 mAh/g (1C discharge) |
| Cycle life | 1C discharge cycle 100, the capacity > 90% |
| Appearance | Black Powder, No Agglomeration, No Sundries |
LiCoO2 (Lithium Cobalt Oxide) powder is used for Li-ion battery cathode material.
Note:Please keep the powder in vacuum box to avoid moisture.
Please bake the powder in vacuum oven at 120 0C – 150 0C before making slurry and coating to ensure maximum capacity.
| Chemical Formula | LiCoO2 |
| Fe | < 0.0100 |
| Ni | < 0.0200 |
| Mn | < 0.0100 |
| Cu | < 0.0050 |
| Ca | < 0.0100 |
| Containing water of moisture | < 0.0500 |
| pH Data | 9 – 11.5 |
| BET surface area | < 0.5 m2/g |
| Tap Density | 2.4 – 2.9 g/cm3 |
| Diameter | D50 : 11 ± 2 µm D50 : > 4 µm |
LiFePO4 (Lithium Iron Phosphate Oxide) powder is used for Li-ion battery cathode material.
Note: Please keep the powder in vacuum box to avoid moisture.
Please bake the powder in vacuum oven at 120 0C – 150 0C before making slurry and coating to ensure maximum capacity.
SPECIFICATIONS:
| Chemical Formula | LiFePO4 |
| Granularity | D10: >0.6 µmD50: 3.0 ~ 5.0 µmD90: <15 µmDmax: <100 µm |
| Pressed Density | > 0.8 g/cm3 |
| Specific Surface Area | 15 ± 3 m2/g |
| Li | 4.3 ± 0.5 % |
| Fe | 33.5 ± 1.5 % |
| P | 19.5 ± 1.0 % |
| C | 1.5 ± 0.3 % |
| Mn | < 0.2 % |
| Na | < 0.1 % |
| Ca | < 0.1 % |
| pH | 9 ~ 11 |
| Moisture | < 0.5 |
| Capacity | > 130 mAh/g (coin cell, 0.2C discharge) |
| Cycle life | 1 C discharge cycle 100, the capacity > 95% |
| Appearance | Black Powder, No Agglomeration, No Sundries |
| Storage Safety | Avoid moist |