Platinum Coated Test Cell Counter Electrode with Fill Hole:

 

glassn1

Platinum Coated Test Cell Counter Electrodes with Fill Hole are used as cathodes in the construction of sealed DSC Test Cells for material set optimization and characterization.

Platinum Coated Test Cell Counter Electrodes with Fill Hole use TEC15 conductive glass and are screen printed with Pt1 Platinum Catalyst which is sintered to produce a transparent, highly active catalytic layer for the electrochemical reduction of I3– to I– in DSC devices.?

Specifications:

Glass Type TEC15 (FTO)
Conducting Layer PT1 Platinum Paste
Sheet Thickness 3.2 mm
Electrode Area When Pre-Cut 30 mm x 20 mm
Printed Area 20 mm x 20 mm

 

Product Size
MS001651 30 mm x 180 mm x 3.2 mm

line

TEC15 Glass Plates:

 

glassn2

TEC15 Glass Plates are an ideal substrate for high-performing DSCs under average sun levels.

TEC15 Glass Plates are transparent conductive glass plates with a range of options for both sheet size and sheet thickness. The sheet resistance of the conductive coating is approximately 15Ω/sq.

Soda-lime glass: The chemical and physical properties of soda-lime glass make it suitable for visible light and DSC applications. The nominally colourless glass transmits a very high percentage of visible light.

Specifications:

Glass Type Soda-lime
Conducting Layer FTO (Fluorine doped tin oxide)
Sheet Resistance 15 Ω/sq
Sheet Thickness 2.2 mm option or 3.2 mm option

 

Product Size
MS001670 100 mm x 100 mm x 3.2 mm x 1 plate
MS001670-10 100 mm x 100 mm x 3.2 mm x 10 plate pack
MS001675 100 mm x 100 mm x 2.2 mm x 1 plate
MS001675-10 100 mm x 100 mm x 2.2 mm x 10 plate pack
MS001680 300 mm x 300 mm x 3.2 mm x 1 plate
MS001680-5 300 mm x 300 mm x 3.2 mm x 5 plate pack
MS001685 300 mm x 300 mm x 2.2 mm x 1 plate
MS001685-5 300 mm x 300 mm x 2.2 mm x 5 plate pack

line

TEC7 Glass Plates:

 

glassn2

TEC7 Glass Plates are an ideal substrate for high-performing DSCs under high sun levels.

TEC7 Glass Plates are transparent conductive glass plates with a range of options for both sheet size and sheet thickness. The sheet resistance of the conductive coating is approximately 7Ω/sq.

Soda-lime glass: The chemical and physical properties of soda-lime glass make it suitable for visible light and DSC applications. The nominally colourless glass transmits a very high percentage of visible light.

Specifications:

Glass Type Soda-lime
Conducting Layer FTO (Fluorine doped tin oxide)
Sheet Resistance 7 Ω/sq
Sheet Thickness 2.2 mm

 

Product Size
MS001790 100 mm x 100 mm x 1 plate
MS001790-10 100 mm x 100 mm x 10 plate pack
MS001795 300 mm x 300 mm x 1 plate
MS001795-5 300 mm x 300 mm x 5 plate pack

line

TEC8 Glass Plates:

 

glassn2

TEC8 Glass Plates are an ideal substrate for high-performing DSCs under high sun levels.

TEC8 Glass Plates are transparent conductive glass plates with a range of options for both sheet size and sheet thickness. The sheet resistance of the conductive coating is approximately 8Ω/sq.

Soda-lime glass: The chemical and physical properties of soda-lime glass make it suitable for visible light and DSC applications. The nominally colourless glass transmits a very high percentage of visible light.

Specifications:

Glass Type Soda-lime
Conducting Layer FTO (Fluorine doped tin oxide)
Sheet Resistance 8 Ω/sq
Sheet Thickness 2.2 mm option or 3.2 mm option

 

Product Size
MS001690 100 mm x 100 mm x 3.2 mm x 1 plate
MS001690-10 100 mm x 100 mm x 3.2 mm x 10 plate pack
MS001695 100 mm x 100 mm x 2.2 mm x 1 plate
MS001695-10 100 mm x 100 mm x 2.2 mm x 10 plate pack
MS001700 300 mm x 300 mm x 3.2 mm x 1 plate
MS001705 300 mm x 300 mm x 2.2 mm x 1 plate
MS001705-5 300 mm x 300 mm x 3.2 mm x 5 plate pack

line

TiO2 Coated Test Cell Glass Electrodes (Opaque):

 

glassblack

TiO2 Coated Test Cell Glass Electrodes (Opaque) are used as anodes in the construction of DSC Test Cells for material set optimization and characterization.

TiO2 Coated Test Cell Glass Electrodes (Opaque) use TEC15 conductive glass, screen printed with Dyesol’s DSL 18NR-AO Active Opaque Titania paste which is sintered to produce an opaque ~15μm semiconductor suitable for Dye Absorption in DSC devices.

Specifications:

Glass Type TEC15, TEC8 (FTO)
Sheet Thickness 3.2 mm
Printed Layer 18NR-AO Active Opaque Titania Paste
Layer Thickness 14 µm ± 1 µm
Printed Active Layer 8 mm x 11 mm
Electrode Area When Pre-Cut 20 mm x 23 mm

 

Product Size
MS001610 161 mm x 80 mm x 3.2 mm

line

TiO2 Coated Test Cell Glass Electrodes (Transparent):

 

glassblack2

TiO2 Coated Test Cell Glass Electrodes (Transparent) are used as anodes in the construction of DSC Test Cells for material set optimization and characterization.

TiO2 Coated Test Cell Glass Electrodes (Transparent) use TEC15 or TEC8 conductive glass, screen printed with Dyesol’s DSL 18NR-T Transparent Titania paste which is sintered to produces a Transparent an ~12μm transparent semiconductor suitable for Dye Absorption in DSC devices.

Specifications:

Glass Type TEC15, TEC8 (FTO)
Sheet Thickness 3.2 mm
Printed Layer 18NR-AO Transparent Titania Paste
Layer Thickness 12 µm ± 1 µm
Printed Active Layer 8 mm x 11 mm
Electrode Area When Pre-Cut 20 mm x 23 mm

 

Product Size
MS001630 161 mm x 80 mm x 3.2 mm